            Common stainless steel wire is 304 stainless steel wire, 304 is 0cr18ni9. (percentage) type of stainless steel, generally 201 202 304 316 These 202 and 304 are used more.Stainless Steel Wire

            316 and 317 stainless steel (317 stainless steel performance after see) is a molybdenum-containing stainless steel species. The molybdenum content of 317 stainless steel is slightly superior to 316 stainless steel. Because of the molybdenum in steel, the total performance of the grade is better than 310 and 304 stainless steel, and when the concentration of sulfuric acid is lower than 15% and higher than 85%, 316 stainless steel has a wide range of uses. 316 stainless steel also has good and chloride erosion properties, so it is usually used in marine environments. 316L Stainless Steel maximum carbon content of 0.03, can be used for welding can not be annealed and the need for maximum corrosion resistance of the use.

           Corrosion Resistance: corrosion resistance is better than 304 stainless steel, in pulp and paper production process has a good corrosion resistance. and 316 stainless steel is also resistant to the erosion of marine and erosive industrial atmospheres.

           Heat resistance: 1600 degrees below the intermittent use and in 1700 degrees below the continuous use, 316 stainless steel has good oxidation resistance. In the 800-1575-degree range, it is best not to continuously effect 316 stainless steel, but in the temperature range of continuous use of 316 stainless steel, the stainless steel with good heat resistance. 316L stainless steel resistance to carbide precipitation is better than 316 stainless steel, can be used above the temperature range.Stainless Steel Wire

          Heat treatment: annealing within a temperature range of 1850-2050 degrees, then quickly annealing, then cooling quickly. 316 stainless steel can not be overheated for hardening.Stainless Steel Wire

          Welding: 316 stainless steel has good weldability. All standard welding methods can be used for welding. Welding can be used according to use, respectively, using 316Cb, 316L or 309Cb stainless steel filler rods or electrodes for welding. In order to obtain the best corrosion resistance, the welding section of 316 stainless steel needs to be welded back fire treatment. If 316L stainless steel is used, no soldering back fire treatment is required.Stainless Steel Wire